Nickel alloys Manual electrode ERNiCrMo-3(Mod) Soldering yekubatanidza
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Fe | Nb+Ti |
MUENZANISO VALUE | 0.01 | 0.12 | 0.44 | 21.7 | 62.7 | 8.25 | 0.003 | 0.003 | 0.9 | 3.41 |
MACHANICAL PROPERTY:
PROPERTY | KUNYANYA SIMBA(MPa) | KUWEDZERA SIMBA(MPa) | IMAPACT VALUE J/℃ | ELONGATION(%) | ||||
MUENZANISO VALUE | - | 765 | - | 38 |
Iyo yakanyanya kuumbwa ndeye 61Ni-22Cr-9Mo-3.5Nb + Ta, iyo inonyanya kushandiswa nickel-chromium-molybdenum welding zvinhu.
Kana iyo yekuzvidzivirira yeTIG welding wire iri welding, iyo inodzivirira inovhara inopinda mukati kuseri kwechidziva che weld, uye inogadzira dense yekudzivirira layer yakafanana kumberi nekumashure kweweld passage, kuitira kuti mativi ese enzira ye weld are. kwete oxidized.Iyo imwe-side welding inoumbwa pamativi ese, uye welding slag inodonha otomatiki mushure mekunge weld passage yatonhodzwa.
Nzira yewelding yewaya yakangofanana neyakajairika nickel based argon arc welding wire.Iyo yakakosha yekupfekedza pamusoro haina kukanganisa kune weldability uye mechanical properties.Iyo arc yakagadzikana, kuumbwa kwakanaka, uye kuyerera kwesimbi inopisa kwakanaka.
-
Shaanxi Pucheng -50 ℃ propane spherical tank project
-
2.3 miriyoni madhiramu eSBM Fast4ward FPSO
-
Shandong Nuclear simba CV20
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Fe | Nb+Ti |
MUENZANISO VALUE | 0.01 | 0.12 | 0.44 | 21.7 | 62.7 | 8.25 | 0.003 | 0.003 | 0.9 | 3.41 |
MACHANICAL PROPERTY:
PROPERTY | KUNYANYA SIMBA(MPa) | KUWEDZERA SIMBA(MPa) | IMAPACT VALUE J/℃ | ELONGATION(%) | ||||
MUENZANISO VALUE | - | 765 | - | 38 |