Low-alloy steels Flux cored wire E81T1-B6C Welding jointing
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T RULES | 0.05-0.12 | 1.25 | 1.00 | 4.0-6.0 | 0.40 | 0.45-0.65 | 0.03 | 0.03 | 0.50 |
AWS Mitemo | 0.05-0.12 | 1.25 | 1.00 | 4.0-6.0 | 0.40 | 0.45-0.65 | 0.03 | 0.03 | 0.50 |
MUENZANISO VALUE | 0.055 | 0.7 | 0.3 | 5 | 0.02 | 0.55 | 0.005 | 0.005 | 0.01 |
MACHANICAL PROPERTY:
PROPERTY | KUNYANYA SIMBA(MPa) | KUWEDZERA SIMBA(MPa) | IMAPACT VALUE J/℃ | ELONGATION(%) | Kurapa kupisa°Cxh | |||||
GB/T RULES | 470 | 550-690 | - | 17 | 745*2 | |||||
AWS Mitemo | 470 | 550-690 | - | 19 | 745*2 | |||||
MUENZANISO VALUE | 585 | 655 | 60/Normal tembiricha | 22 | 745*2 |
AKAKUDZWA WEDDING PARAMETERS:
DIAMETERS ZVINOTAURWA(mm) | 1.2 | ||||
Volt | 24-35 | ||||
Amp | 160-320 | ||||
Hurefu hwekuwedzera hwakaoma(mm) | 15-20 | ||||
Kuyerera kwegasi(l/min) | 15-25 |
Iyo arc yakapfava uye yakagadzikana, kushoma kupfava, kwakanaka kuumba.
Kubvisa zvakanaka slag, shoma soot.
Neyakanakisa welding process performance.
Zhangjiagang CIMC Sundayin Cryogenic Equipment Co., LTD.Cryogenic Container (LNG Kuzadza chiteshi)
Tangshan LNG pombi yekuburitsa pombi chirongwa
CHEMICAL COMPONET:
ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T RULES | 0.05-0.12 | 1.25 | 1.00 | 4.0-6.0 | 0.40 | 0.45-0.65 | 0.03 | 0.03 | 0.50 |
AWS Mitemo | 0.05-0.12 | 1.25 | 1.00 | 4.0-6.0 | 0.40 | 0.45-0.65 | 0.03 | 0.03 | 0.50 |
MUENZANISO VALUE | 0.055 | 0.7 | 0.3 | 5 | 0.02 | 0.55 | 0.005 | 0.005 | 0.01 |
MACHANICAL PROPERTY:
PROPERTY | KUNYANYA SIMBA(MPa) | KUWEDZERA SIMBA(MPa) | IMAPACT VALUE J/℃ | ELONGATION(%) | Kurapa kupisa°Cxh | |||||
GB/T RULES | 470 | 550-690 | - | 17 | 745*2 | |||||
AWS Mitemo | 470 | 550-690 | - | 19 | 745*2 | |||||
MUENZANISO VALUE | 585 | 655 | 60/Normal tembiricha | 22 | 745*2 |
AKAKUDZWA WEDDING PARAMETERS:
DIAMETERS ZVINOTAURWA(mm) | 1.2 | ||||
Volt | 24-35 | ||||
Amp | 160-320 | ||||
Hurefu hwekuwedzera hwakaoma(mm) | 15-20 | ||||
Kuyerera kwegasi(l/min) | 15-25 |